This PhD thesis characterises the damage that occurs in tungsten when it is exposed to a fusion-like environment. The book presents pioneering work on the use of grazing-incidence small-angle X-ray scattering (GISAXS) to measure nano-bubble formation in tungsten exposed to helium plasma. The phenomenon of nanoscale bubble formation within metals during helium plasma exposure can lead to undesirable changes in the material properties, such as complex nanoscale surface modification or a reduction in thermal conductivity.

This PhD thesis characterises the damage that occurs in tungsten when it is exposed to a fusion-like environment. The book presents pioneering work on the use of grazing-incidence small-angle X-ray scattering (GISAXS) to measure nano-bubble formation in tungsten exposed to helium plasma. The phenomenon of nanoscale bubble formation within metals during helium plasma exposure can lead to undesirable changes in the material properties, such as complex nanoscale surface modification or a reduction in thermal conductivity.

This PhD thesis characterises the damage that occurs in tungsten when it is exposed to a fusion-like environment. The book presents pioneering work on the use of grazing-incidence small-angle X-ray scattering (GISAXS) to measure nano-bubble formation in tungsten exposed to helium plasma. The phenomenon of nanoscale bubble formation within metals during helium plasma exposure can lead to undesirable changes in the material properties, such as complex nanoscale surface modification or a reduction in thermal conductivity.